Carbon/Carbon Fiber Board
Product Description:
Carbon/carbon box plates are specifically designed for high-temperature graphitization box furnace applications, crafted from carbon/carbon composite materials. They boast a range of outstanding properties, including stable electrical resistance, exceptional wear resistance, excellent thermal shock resistance, and significantly larger volumetric capacity. These features make them an outstanding choice as high-temperature thermal field materials—and they represent an upgraded alternative to traditional graphite box plates.
Application areas:
Graphitization of graphite as a negative electrode material for lithium batteries
| Recommended grades: |
KBC-XTT |
| Density, g/cm³: |
≥1.55 |
| Room-temperature resistivity, μΩ·m: |
≤35 |
| Flexural strength, MPa: |
≥15 |
| Compressive strength, MPa: |
≥30 |
| Coefficient of thermal expansion, 10 -6 /K |
≤2 |
Keywords:
Category:
Related Products
Pre-fused needle-shaped coke single particles
| Recommended grades: | KG-C01H | ||
| Project: | Indicator Range | Typical value | Detection Instruments and Methods |
| Particle size D50, μm: | 11.0 ± 1.5 | 11.163 | Malvern 3000 Laser Particle Sizer |
| Tapped density, g/cm³ 3： | ≥1.0 | 1.28 | BT-312 Vibration Tapped Density Tester |
| Specific surface area, m² 2 /g: | ≤2.0 | 1.15 | BSD-BET400 Surface Area Analyzer |
| Ash content, %: | ≤0.1 | 0.01 | Muffle furnace, calcined at 900°C for 2-3 hours until constant weight. |
| Graphitization degree, %: | ≥93.5 | 94.5 | XRD X-ray Diffractometer |
| First discharge capacity, mAh/g: | ≥348.0 | 354.22 | Button cell battery |
| First Coulombic efficiency, %: | ≥94.0 | 94.95 | Button cell battery |
| Magnetic material, ppm: | ≤1 | 0.16 | ICP |
Pre-fused needle-shaped coke single particles
| Recommended grades: | KG-C02H | ||
| Project: | Indicator Range | Typical value | Detection Instruments and Methods |
| Particle size D50, μm: | 14.5 ± 1.5 | 14.852 | Malvern 3000 Laser Particle Sizer |
| Tapped density, g/cm³ 3： | ≥1.15 | 1.28 | BT-312 Vibration Tapped Density Tester |
| Specific surface area, m² 2 /g: | ≤2.0 | 1.12 | BSD-BET400 Surface Area Analyzer |
| Ash content, %: | ≤0.1 | 0.01 | Muffle furnace, burn at 900℃ for 2-3 hours until constant weight. |
| Graphitization degree, %: | ≥94.0 | 94.7 | XRD X-ray Diffractometer |
| First discharge capacity, mAh/g: | ≥355.0 | 355.47 | Button cell |
| First Coulombic efficiency, %: | ≥94.0 | 94.83 | Button cell |
| Magnetic material, ppm: | ≤1 | 0.13 | ICP |
Secondary Particles of Needle-Shape Coke Before Calcination
| Recommended grades: | KG-C03B | ||
| Project: | Indicator Range | Typical value | Detection Instruments and Methods |
| Particle size D50, μm: | 15.5 ± 1.5 | 15.557 | Malvern 3000 Laser Particle Sizer |
| Tapped density, g/cm³ 3： | ≥1.0 | 1.14 | BT-312 Vibration Tapped Density Tester |
| Specific surface area, m² 2 /g: | ≤2.0 | 1.34 | BSD-BET400 Surface Area Analyzer |
| Ash content, %: | ≤0.1 | 0.01 | Muffle furnace, burn at 900℃ for 2-3 hours until constant weight. |
| Graphitization degree, %: | ≥94.0 | 94.3 | XRD X-ray Diffractometer |
| First discharge capacity, mAh/g: | ≥350.0 | 351.64 | Button cell battery |
| First Coulombic efficiency, %: | ≥94.0 | 94.27 | Button cell battery |
| Magnetic material, ppm: | ≤1 | 0.12 | ICP |
Secondary Granules of Calcined Petroleum Coke, Standard Model
| Recommended grades: | KG-C06B | ||
| Project: | Indicator Range | Typical value | Detection Instruments and Methods |
| Particle size D50, μm: | 14.5 ± 1.5 | 14.992 | Malvern 3000 Laser Particle Sizer |
| Tapped density, g/cm³ 3： | ≥1.0 | 1.11 | BT-312 Vibration Tapped Density Tester |
| Specific surface area, m² 2 /g: | ≤2.0 | 1.37 | BSD-BET400 Surface Area Analyzer |
| Ash content, %: | ≤0.1 | 0.01 | Muffle furnace, burn at 900℃ for 2-3 hours until constant weight. |
| Graphitization degree, %: | ≥92.5 | 93.1 | XRD X-ray Diffractometer |
| First discharge capacity, mAh/g: | ≥345.0 | 346.41 | Button cell battery |
| First Coulombic efficiency, %: | ≥94.0 | 94.39 | Button cell battery |
| Magnetic material, ppm: | ≤1 | 0.23 | ICP |
Secondary-particulate, High-Capacity Grade Calcined Petroleum Coke
| Recommended grades: | KG-C06B | ||
| Project: | Indicator Range | Typical value | Detection Instruments and Methods |
| Particle size D50, μm: | 14.5 ± 1.5 | 14.204 | Malvern 3000 Laser Particle Sizer |
| Tapped density, g/cm³ 3： | ≥1.0 | 1.13 | BT-312 Vibration Tapped Density Tester |
| Specific surface area, m² 2 /g: | ≤2.0 | 1.35 | BSD-BET400 Surface Area Analyzer |
| Ash content, %: | ≤0.1 | 0.01 | Muffle furnace, burn at 900℃ for 2-3 hours until constant weight. |
| Graphitization degree, %: | ≥92.5 | 93.8 | XRD X-ray Diffractometer |
| First discharge capacity, mAh/g: | ≥350.0 | 351.27 | Button cell battery |
| First Coulombic efficiency, %: | ≥94.0 | 94.89 | Button cell battery |
| Magnetic material, ppm: | ≤1 | 0.18 | ICP |
Calcined Petroleum Coke Single Particles
| Recommended grades: | KG-C10H | ||
| Project: | Indicator Range | Typical value | Detection Instruments and Methods |
| Particle size D50, μm: | 16.0 ± 1.5 | 16.18 | Malvern 3000 Laser Particle Sizer |
| Tapped density, g/cm³ 3： | ≥1.0 | 1.21 | BT-312 Vibration Tapped Density Tester |
| Specific surface area, m² 2 /g: | ≤2.0 | 1.66 | BSD-BET400 Surface Area Analyzer |
| Ash content, %: | ≤0.1 | 0.01 | Muffle furnace, burn at 900℃ for 2-3 hours until constant weight. |
| Graphitization degree, %: | ≥93.5 | 94.3 | XRD X-ray Diffractometer |
| First discharge capacity, mAh/g: | ≥348.0 | 349.86 | Button cell |
| First Coulombic efficiency, %: | ≥94.0 | 95.06 | Button cell |
| Magnetic material, ppm: | ≤1 | 0.11 | ICP |
Get a free product quote